heat distortion temperature | 40~50 °C | 40~50 °C | 40~50 °C | 40~50 °C | 80~100 °C | 120~150 °C | 120~150 °C | 50~50 °C | density 8 | density 2.7 |
min wall thickness | 0.6mm | 0.6mm | 0.6mm | 0.6mm | 0.6mm | 0.5mm | 0.5mm | 0.5mm | 0.5mm | 0.5mm |
Minimum hole diameter | 1mm | 1mm | 1mm | 1mm | 1mm | 1.2mm | 1.2mm | 0.8mm | 0.8mm | 0.8mm |
Material Hardness(Shore D) | 79 | 87 | 85 | 80 | 85 | 86 | 75 | 79 | 158HB | 120HB |
Tensile Strength (stretch) | 47Mpa | 50Mpa | 38~56Mpa | 48Mpa | 40~44Mpa | 50Mpa | 52Mpa | 47Mpa | 560Mpa | 330Mpa |
Tensile Strength (fracture) | 33~40Mpa | 56Mpa | 60Mpa | 56Mpa | 52Mpa | 70Mpa | 52Mpa | 30~40Mpa | 10~12% | 0.06 |
Bending Strength | 67Mpa | 84Mpa | 69~74Mpa | 68Mpa | 64~69Mpa | 75~80Mpa | 52Mpa | 67Mpa | 480Mpa | 245Mpa |
Bending Modulus | 2178~2222Mpa | 2490Mpa | 2692~2775Mpa | 2300Mpa | 2900~3200Mpa | 2800Mpa | 1500mpa ISO178 | Mpa | 180GPa | 70GPa |
Print layer height | 0.1mm/0.05mm | 0.1mm | 0.1mm | 0.1mm | 0.1mm | 0.08mm | 0.08mm | 0.02mm | | |
Printing Error Rate | 1%~3% | 1%~3% | 1%~3% | 1%~3% | 1%~3% | 2.5% | 2.5% | 0.001 | 0.1%~0.2% | 0.1%~0.2% |
Surface layer | smoothing | thick bottom | smoothing | thick bottom | smoothing | Rough | Rough | fine smooth | Natural pitting | Natural pitting |